Customizable HDPE Smooth Geomembrane for Your Specific Needs and Requirement
Product Introduction
The high density polyethylene resin is a waterproof barrier material, which has excellent environmental stress cracking resistance, low temperature resistance, aging resistance and corrosion resistance.
Product Properties
HDPE geomembrane is widely used in various fields due to its excellent chemical stability and mechanical strength. It can resist the corrosion of various chemicals, including acids, alkalis, salts, etc. In addition, it has good tensile strength and elongation at break, making it suitable for use under various harsh geological and climatic conditions.
Product Application
The main applications of HDPE geomembrane include but are not limited to the following aspects:
Landfill Liner: Prevents leachate from landfills from polluting groundwater.
-
Solid Waste Landfill Imperviousness: Used for the impervious treatment of solid waste landfills.
-
Wastewater Treatment Plant Imperviousness: Preventing wastewater seepage to protect the environment.
-
Artificial Lake Waterproofing: For waterproofing treatment of artificial lakes.
-
Tailings Processing: Preventing tailings wastewater from polluting the environment.
-
Hydraulic Engineering: Such as dams, cofferdams, canals, reservoirs, etc.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification |
0.75mm |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
Remark |
| Item |
| Thickness (mm) |
0.75mm |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
|
| Density (g/c㎡,≥) |
0.939 |
|
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) |
11 |
15 |
18 |
22 |
29 |
37 |
44 |
|
| Breaking Strength (N/mm,LD/TD) |
20 |
27 |
33 |
40 |
53 |
67 |
80 |
|
| Yeild Elongation Rate (%) |
12 |
|
| Breaking Elongation Rate (%) |
700 |
|
| Rectangular Tear Strength (N) |
93 |
125 |
156 |
187 |
249 |
311 |
374 |
|
| Puncture Strength (N) |
240 |
320 |
400 |
480 |
640 |
800 |
960 |
|
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) |
300 |
|
| Carbon Black |
| Carbon Black Content(Rang) (%) |
2.0~3.0 |
|
| Carbon Black Dispersion |
Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 |
|
| Oxidative Induction Time (OIT) |
| Standard OIT (min) |
100 |
|
| High Pressure OIT (min) |
400 |
|
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) |
55 |
|
| 90 days after baking, the hight pressure OIT retention(%) |
80 |
|
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) |
50 |
|
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) |
50 |
|
| -70℃ The Low Temperature Embrittlement Performance mpact |
Pass |
|
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) |
≤1.0X10-13 |
|
| Dimensional Stability |
±2 |
|
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
Specification
Item |
0.30 |
0.50 |
0.75 |
1.00 |
1.25 |
1.50 |
2.00 |
2.50 |
3.00 |
Remark |
| Thickness (mm) |
0.30 |
0.50 |
0.75 |
1.00 |
1.25 |
1.50 |
2.00 |
2.50 |
3.00 |
|
| Density (g/c㎡,≥) |
0.94 |
| Tensile Yield Strength (N/mm, ≥,LD/TD) |
4 |
7 |
10 |
13 |
16 |
20 |
26 |
33 |
40 |
|
| Tensile Breaking Strength (N/mm, ≥,LD/TD) |
6 |
10 |
15 |
20 |
25 |
30 |
40 |
50 |
60 |
|
| Yield Elongation Rate (%,≥,LD/TD) |
- |
- |
- |
11 |
|
| Breaking Elongation Rate (%,≥,LD/TD) |
600 |
|
| Rectangular Tear Load (N,≥,LD/TD) |
34 |
56 |
84 |
115 |
140 |
170 |
225 |
280 |
340 |
|
| Puncture Strength (N,≥) |
72 |
120 |
180 |
240 |
300 |
360 |
480 |
600 |
720 |
|
| Carbon Black Content (%) |
2.0~3.0 |
|
| Carbon Black Dispersion |
Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not allowed |
|